T1 - Transparent organic light-emitting diodes with top electrode using ion-plating method
AU - Sano, Hironao
AU - Ishida, Ryota
AU - Kura, Tatsuya
AU - Fujita, Shunsuke
AU - Naka, Shigeki
AU - Okada, Hiroyuki
AU - Takai, Takeshi
N1 - Publisher Copyright:
© 2015 The Institute of Electronics, Information and Communication Engineers.
PY - 2015/11
Y1 - 2015/11
N2 - Transparent organic light-emitting diodes (TOLEDs) were investigated with top electrode of indium-tin-oxide (ITO) by ion-plating method. High deposition rate of 4.4 nm/s was realized without plasma damage of under organic layer. In the TOLEDs with inverted structure, high transmittance of over 75% at 550 nm and bright emission of 1,850 and 1,410 cd/m2, from bottom and top side at 163 mA/cm2, respectively, were obtained.
AB - Transparent organic light-emitting diodes (TOLEDs) were investigated with top electrode of indium-tin-oxide (ITO) by ion-plating method. High deposition rate of 4.4 nm/s was realized without plasma damage of under organic layer. In the TOLEDs with inverted structure, high transmittance of over 75% at 550 nm and bright emission of 1,850 and 1,410 cd/m2, from bottom and top side at 163 mA/cm2, respectively, were obtained.
KW - High deposition rate
KW - Ion-plating
KW - Low temperature deposition
KW - Organic light-emitting diode
KW - Transparent electrode
UR - http://www.scopus.com/inward/record.url?scp=84947938558&partnerID=8YFLogxK
U2 - 10.1587/transele.E98.C.1035
DO - 10.1587/transele.E98.C.1035
M3 - 学術論文
AN - SCOPUS:84947938558
SN - 0916-8524
VL - E98C
SP - 1035
EP - 1038
JO - IEICE Transactions on Electronics
JF - IEICE Transactions on Electronics
IS - 11
ER -