Observation of Internal Fatigue Cracks in Repeatedly Induction-Heated S45C Bearing Steel under Rotating Bending Fatigue

Keyphrases

• Rotating Bending Fatigue Test 100%
• Bearing Steel 100%
• S45C 100%
• Internal Fatigue Crack 100%
• Soft Layer 66%
• Hard Layer 50%
• Pearlite 33%
• Microstructure 16%
• Heating Process 16%
• Fatigue Strength 16%
• High Fatigue Strength 16%
• Fracture Surface 16%
• Induction Heating 16%
• Low Carbon Steel 16%
• Ferrite 16%
• Cyclic Stress Ratio 16%
• Repeated Heating 16%

Engineering

• Bearing Steel 100%
• Internals 100%
• Fatigue Crack 100%
• Fatigue Strength 33%
• Pearlite 33%
• Hard Layer 33%
• Mechanical Fatigue Test 16%
• Fracture Surface 16%
• Mild Steel 16%
• Cyclic Stress 16%
• Induction Heating 16%

Material Science

• Bearing Steel 100%
• Fatigue Crack 100%
• Low Carbon Steel 16%