Visualization of Magnetization Transfer Effect in Polyethylene Glycol Impregnated Waterlogged Wood

To visualize the condition of impregnation of polyethylene glycol (PEG) in waterlogged wood, we demonstrated magnetic transfer (MT) magnetic resonance imaging (MRI) through a series of process of PEG impregnation. Three different samples were examined; reference wood, 10 cm cut wood, and 5 cm cut wood. During this study, the upper section sample was kept immersed in water, for the middle and lower sections the concentration of PEG solution was changed at 20 wt% intervals from 20 to 100 wt%. The impregnated periods of each PEG solution concentration were 14 days. Then, MR imaging were performed with/without MT pulse. The MTR value for both 10 cm- and 5 cm-samples were shown to decrease at 20 wt% PEG at peak concentration. When the sample volume was large, e.g., 10 cm-sample, the MTR value decreased to 100 wt% PEG concentration. In contrast, when a sample volume was small, e.g., 5 cm-sample, MTR value decreased to 60 wt% PEG concentration. In conclusion, MTR analysis makes it possible to nondestructively visualize and evaluate the inner condition concerning the PEG impregnation method for waterlogged wood.