Simultaneous nano-texturing onto a cvd-diamond coated piercing punch with femtosecond laser trimming

In this study, a CVD (Chemical Vapor Deposition)-diamond coated tungsten carbide cobalt (WC (Co) punch was trimmed to adjust its surface roughness and to significantly reduce its edge curvature for fine piercing by femtosecond laser processing. Through this laser trimming, the surface quality of the diamond coating and the punch edge profile were improved to less than 0.5 μm at the maximum roughness and 2 μm in the edge width, respectively. In parallel with this improvement of surface quality, the side surface of the diamond coating was modified to include nano-textures via the LIPSS (Laser Induced Periodic Surface Structuring) process. Through the fine piercing process, this nanotexture was transcribed onto the pierced hole surface together with fine shearing of the hole by piercing. WLI (White-Light Interferometry) and SEM (Scanning Electron Microscopy) were utilized to describe this transcription of nanotextures during the piercing process. These semiregular nanotextures with an LIPSS period of 300 nm on the pierced hole surface induced a blue colored surface plasmon.