Microstructure evolution in a hydrogen charged and aged Al–Zn–Mg alloy

Artenis Bendo*, Kenji Matsuda, Seungwon Lee, Katsuhiko Nishimura, Hiroyuki Toda, Kazuyuki Shimizu, Tomohito Tsuru, Masatake Yamaguchi

*この論文の責任著者

研究成果: ジャーナルへの寄稿総説査読

12 被引用数 (Scopus)

抄録

Microstructure evolution of alloy with composition Al – 3.4 Zn – 1.9 Mg (at. %) was tracked using high resolution imaging and electron diffraction during ageing at 120 °C after being initially natural aged for 4 days. Hydrogen was charged in microstructure by cutting samples in Electrical Discharge Machine immediately after being quenched from solid solution temperature. Transmission Electron Microscope observations revealed a higher presence of high aspect ratio GPII-zones in microstructure of hydrogen charged and aged samples. Correlation was made with previously reported hydrogen effect into vacancy formation.

本文言語英語
ページ(範囲)50-56
ページ数7
ジャーナルMaterialia
3
DOI
出版ステータス出版済み - 2018/11

ASJC Scopus 主題領域

  • 材料科学一般

フィンガープリント

「Microstructure evolution in a hydrogen charged and aged Al–Zn–Mg alloy」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル