Hydrogenation of CO₂to LPG over CuZnZr/MeSAPO-34 catalysts

The utilization of CO₂to synthesize environmentally benign liquid fuels offers a solution to replacing depleting petroleum resources. Herein, a ternary CuZnZr (CZZ) metal oxide catalyst and a SAPO-34 zeolite were synthesized by co-precipitation and hydrothermal synthesis, respectively. Different metals were impregnated into the latter to obtain MeSAPO-34 (Me = Mn, Zn and Zr). A granule mixture of CZZ and MeSAPO-34 components (CZZ/MeSAPO-34 catalyst) was then effectively utilized in a tandem catalytic process for one-step CO₂hydrogenation to liquefied petroleum gas (LPG). The CZZ/MeSAPO-34 catalysts were characterized by using XRD, H₂-TPR, BET, SEM-EDS and NH₃-TPD techniques. SEM-EDS and XRD results indicated that an appropriate amount of Zr metal loading induced minimum zeolite framework collapse compared to a similar amount of Mn and Zn, which was more favorable for higher activity. In addition, NH₃-TPD results revealed that the acidity of SAPO-34 could be altered after impregnation with different metals in different quantities. Tuning the acid density and strength, together with adjusting the CZZ to MeSAPO-34 weight ratio, had a collectively critical effect on LPG selectivity. An effective hydrogenation microenvironment which favors lower alkane formation (C₃-C₄) was enhanced after the acidity of the molecular sieve was tuned. LPG selectivity could reach 86% over the CZZ/5% ZrSAPO-34 catalyst at 2 MPa, 350 °C, a W/F ratio of 6, a H₂/CO₂ratio of 3 and a weight ratio of 1.