HRTEM observation of the age hardening precipitates in Mg-Zn alloy

Shogo Mori; Tokimasa Kawabata; Kenji Matsuda; Susumu Ikeno

doi:10.4028/0-87849-463-4.157

HRTEM observation of the age hardening precipitates in Mg-Zn alloy

Shogo Mori^*, Tokimasa Kawabata, Kenji Matsuda, Susumu Ikeno

^*この論文の責任著者

材料デザイン工学科

研究成果: ジャーナルへの寄稿 › 会議記事 › 査読

2 被引用数 (Scopus)

抄録

The age hardening precipitates of Mg-4.7mass%Zn alloy aged at 423K,473K were studied by using high-resolution transmission electron microscope (HRTEM). Contrasts of mono layers were confirmed to exist on the (0001) and (11̄00) matrix planes. It was considered that the contrast of mono layer was plate-like shape, and identified as pre-precipitates from as-quenched stage to early stage of aging at 473K for 32h. In the peak aged specimen of aged at 473K, the β₁' phase was observed. The β₁' phase has a rod-like shape and parallel to c-axis of Mg matrix. It can be observed orientation relationship between Mg matrix and β₁'phase has not only same parts to previous reports but also different parts in one β₁' phase.

本文言語	英語
ページ（範囲）	157-160
ページ数	4
ジャーナル	Advanced Materials Research
巻	24-25
DOI	https://doi.org/10.4028/0-87849-463-4.157
出版ステータス	出版済み - 2007
イベント	PRICM 6: The 6th Pacific Rim International Conference on Advanced Materials and Processing - Jeju Island, 大韓民国継続期間: 2007/11/05 → 2007/11/09

ASJC Scopus 主題領域

工学一般

文献へのアクセス

10.4028/0-87849-463-4.157

引用スタイル

@article{04c3c76500cc42aebc8eaeedf79f7274,

title = "HRTEM observation of the age hardening precipitates in Mg-Zn alloy",

abstract = "The age hardening precipitates of Mg-4.7mass%Zn alloy aged at 423K,473K were studied by using high-resolution transmission electron microscope (HRTEM). Contrasts of mono layers were confirmed to exist on the (0001) and (1{\=1}00) matrix planes. It was considered that the contrast of mono layer was plate-like shape, and identified as pre-precipitates from as-quenched stage to early stage of aging at 473K for 32h. In the peak aged specimen of aged at 473K, the β1' phase was observed. The β1' phase has a rod-like shape and parallel to c-axis of Mg matrix. It can be observed orientation relationship between Mg matrix and β1'phase has not only same parts to previous reports but also different parts in one β1' phase.",

keywords = "Aging, High resolution transmission electron microscope, Mg-Zn alloy, Precipitates",

author = "Shogo Mori and Tokimasa Kawabata and Kenji Matsuda and Susumu Ikeno",

year = "2007",

doi = "10.4028/0-87849-463-4.157",

language = "英語",

volume = "24-25",

pages = "157--160",

journal = "Advanced Materials Research",

issn = "1022-6680",

publisher = "Trans Tech Publications",

note = "PRICM 6: The 6th Pacific Rim International Conference on Advanced Materials and Processing ; Conference date: 05-11-2007 Through 09-11-2007",

}

TY - JOUR

T1 - HRTEM observation of the age hardening precipitates in Mg-Zn alloy

AU - Mori, Shogo

AU - Kawabata, Tokimasa

AU - Matsuda, Kenji

AU - Ikeno, Susumu

PY - 2007

Y1 - 2007

N2 - The age hardening precipitates of Mg-4.7mass%Zn alloy aged at 423K,473K were studied by using high-resolution transmission electron microscope (HRTEM). Contrasts of mono layers were confirmed to exist on the (0001) and (11̄00) matrix planes. It was considered that the contrast of mono layer was plate-like shape, and identified as pre-precipitates from as-quenched stage to early stage of aging at 473K for 32h. In the peak aged specimen of aged at 473K, the β1' phase was observed. The β1' phase has a rod-like shape and parallel to c-axis of Mg matrix. It can be observed orientation relationship between Mg matrix and β1'phase has not only same parts to previous reports but also different parts in one β1' phase.

AB - The age hardening precipitates of Mg-4.7mass%Zn alloy aged at 423K,473K were studied by using high-resolution transmission electron microscope (HRTEM). Contrasts of mono layers were confirmed to exist on the (0001) and (11̄00) matrix planes. It was considered that the contrast of mono layer was plate-like shape, and identified as pre-precipitates from as-quenched stage to early stage of aging at 473K for 32h. In the peak aged specimen of aged at 473K, the β1' phase was observed. The β1' phase has a rod-like shape and parallel to c-axis of Mg matrix. It can be observed orientation relationship between Mg matrix and β1'phase has not only same parts to previous reports but also different parts in one β1' phase.

KW - Aging

KW - High resolution transmission electron microscope

KW - Mg-Zn alloy

KW - Precipitates

UR - http://www.scopus.com/inward/record.url?scp=57649083589&partnerID=8YFLogxK

U2 - 10.4028/0-87849-463-4.157

DO - 10.4028/0-87849-463-4.157

M3 - 会議記事

AN - SCOPUS:57649083589

SN - 1022-6680

VL - 24-25

SP - 157

EP - 160

JO - Advanced Materials Research

JF - Advanced Materials Research

T2 - PRICM 6: The 6th Pacific Rim International Conference on Advanced Materials and Processing

Y2 - 5 November 2007 through 9 November 2007

ER -

HRTEM observation of the age hardening precipitates in Mg-Zn alloy

抄録

ASJC Scopus 主題領域

文献へのアクセス

フィンガープリント

引用スタイル