Effects of Ag content on the mechanical properties of (Nd,Eu,Gd)-Ba-Cu-O bulk superconductors

K. Katagiri*, A. Murakami, R. Kan, K. Kasaba, K. Noto, M. Muralidhar, N. Sakai, M. Murakami

*この論文の責任著者

研究成果: ジャーナルへの寄稿会議記事査読

16 被引用数 (Scopus)

抄録

In order to investigate the effects of Ag content on the mechanical properties of a high performance melt-processed (Nd,Eu,Gd)Ba2Cu 3Oy single grain bulk superconductors with 30 mol% Gd 2BaCuO5, tensile tests of specimens cut from the bulks have been carried out at room temperature. The tensile strength in the direction perpendicular to the c-axis of the sample with 20 wt.% Ag was higher than that of the sample with 10 wt.% Ag. This is ascribed to a decrease in the void fraction and suppression of cracks by an increased Ag particles revealed by the microstructure image analysis. The almost identical value of Young's modulus obtained for both of the samples are presumably due to the balance of the effects of the voids and soft Ag particles mentioned above. Comparing these results with that in the c-axis direction and that obtained by the compressive test, the anisotropy of the elastic behavior associated with the effect of pre-existing micro-cracks perpendicular to the c-axis was discussed.

本文言語英語
ページ(範囲)526-530
ページ数5
ジャーナルPhysica C: Superconductivity and its Applications
392-396
PART 1
DOI
出版ステータス出版済み - 2003/10
イベントProceedings of the 15th International Symposium on Superconduc - Yokohama, 日本
継続期間: 2002/11/112002/11/13

ASJC Scopus 主題領域

  • 電子材料、光学材料、および磁性材料
  • 凝縮系物理学
  • エネルギー工学および電力技術
  • 電子工学および電気工学

フィンガープリント

「Effects of Ag content on the mechanical properties of (Nd,Eu,Gd)-Ba-Cu-O bulk superconductors」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル